● Mea: 4M● Module: 20CrMnTi● Hoʻoponopono wela: Carburization● Paʻakiki: 58-62HRC● Papa Pono: DIN 7
● Mea: S45C● Module: 2.5M● Heat Treatment: Induction hardening● Paʻakiki: 55HRC● Papa Pono: ISO7
● Mea: 16MnCr5● Module: 1-4M● Hoʻomaʻamaʻa wela: Carburizing● Paʻakiki: 58HRC● Papa Pono: ISO 6
● Mea: 40Cr● Module: 2M● Hoʻoponopono wela: Q&T● Paʻakiki: 35HRC● Papa Pono: ISO6/JIS6
● Mea: 4340H● Module: 6M● Hoʻomaʻamaʻa wela: QPQ Nitriding● Paʻakiki: 800HV● Papa Pono: ISO6
● Mea: 18CrNiMo7-6● Module: 4.5M● Hoʻomaʻamaʻa wela: Carburizing● Paʻakiki: 60HRC● Papa Pono: DIN5
● Mea: 4140H● Module: 3M● Hoʻoponopono wela: Carbonitriding● Paʻakiki: 700HV● Papa Pono: GB7
● Mea: SUS304● Module: 1.5M● Hoʻoponopono Wela: NA● Paʻakikī: 180HB● Papa Pono: DIN6
● Mea: 8620H● Module: 4M● Hoʻomaʻamaʻa wela: Carburizing● Paʻakiki: 58HRC● Papa Pono: ISO6/JIS2
● Mea: 1045● Module: 2M● Heat Treatment: Induction hardening● Paʻakiki: 50HRC● Papa Pono: ISO7
● Mea: 16MnCr5● Module: 3M● Hoʻomaʻamaʻa wela: Carburizing● Paʻakiki: 62HRC● Papa Pono: DIN5
● Mea: Steel 8620H● Module: 3M● Lapaʻau ʻili: Carburization